    題名: Sn-9Zn-(0~4)Ag迴銲於化金基板後在純水中之電化學遷移行為;Electrochemical Migration of Sn-9Zn-(0~4)Ag Reflowed on Cu/Ni/Au Substrate in Pure Water
    作者: 洪宜芳;Yi-Fang Hong
    貢獻者: 機械工程研究所
    關鍵詞: XPS分析;介金屬化合物;電化學遷移;錫鋅銀銲料;陽極動態極化;Sn-Zn-Ag solder;intermetallic compound;XPS;potentiodynamic polarization;electrochemical migration
    日期: 2005-06-07
    上傳時間: 2009-09-21 11:52:25 (UTC+8)
    出版者: 國立中央大學圖書館
    摘要: 摘 要 本研究探討錫-9鋅-(0~4)銀銲料迴銲於化金基板上上之電化學遷移行為,將其完全浸泡於純水溶液中,兩銲球間施以3V~5V直流偏壓,結果顯示:銲料中增加銀含量與提高施加偏壓,皆會造成銲料抗電化學遷移能力下降。 在純水中之陽極動態極化研究結果顯示:本系統銲料之開路電位隨著銀含量增加而微幅上升,且陽極電流隨銲料中的銀含量增加而提高。X光光電子譜儀分析顯示:迴銲後銲錫表面有一層SnO2覆蓋。銲料中銀含量越高,導致主要引起兩極間析出物的鋅與錫兩元素,會隨遷移時間變化其比例亦隨之變化。 錫-9鋅-(0~4)銀銲錫分別在迴銲後爐冷、空冷、油冷、水冷四種情況下,其冷卻速率越快越容易產生電化學遷移行為。從迴銲後不同冷卻速率之XPS分析中發現銲球表面產生氧化層程度不同;從動態極化曲線中發現:當冷卻速率越快,陽極的反應電流越大。 Abstract Electrochemical migration behaviors of the Sn-9Zn-(0~4)Ag solders reflowed on Cu/Ni/Au substrate have been studied. The electrochemical migration resistance of the Sn-9Zn-(0~4)Ag solders at a bias of 3V~5V in pure water decreased with in creasing Ag content from 0 to 4 wt% and electrical bias from 3 to 5 V. The anode potentiodynamic polarization in pure water showed that OCP of Sn-9Zn-(0~4)Ag increased slightly with increasing Ag. The anode current of solders increased with increasing Ag content at the solder ball. From XPS spectra showed that SnO2 oxide covered on the solder balls after reflow. The ratio of Ag in the solder ball caused to migration precipitate between solder balls and the ratio of Zn and Sn changes with time. When Sn-9Zn-(0~4)Ag solder after reflow the cooling rate would increase , the electrochemical resistance will decrease in four cooling state at oven、air、oil、water cooling. From XPS analysis show that solder ball after reflow the surface produced oxide proportion is different at different cooling rate ; from the anode potentiodynamic polarization showed that cooling rate increase the anode reaction increased.
    顯示於類別:[機械工程研究所] 博碩士論文

    文件中的檔案:

    檔案 大小格式瀏覽次數


    在NCUIR中所有的資料項目都受到原著作權保護.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©  2006-2024  - 隱私權政策聲明