| 題名: | Synthesis of Flower-Like NiO and Effects of Morphology on Its Catalytic Properties |
| 作者: | Zhao,B;Ke,XK;Bao,JH;Wang,CL;Dong,L;Chen,YW;Chen,HL |
| 貢獻者: | 化學工程與材料工程學系 |
| 關鍵詞: | NICKEL-OXIDE;THERMAL-DECOMPOSITION;BLOCK-COPOLYMERS;CHEMICAL-SHIFTS;METAL-OXIDES;CO;SURFACE;NO;ROUTE;SIZE |
| 日期: | 2009 |
| 上傳時間: | 2010-06-29 17:28:08 (UTC+8) |
| 出版者: | 中央大學 |
| 摘要: | NiO with novel flower-like morphology was prepared by using a two-step, template- and surfactant-free, environmentally friendly method. Flower-like NiO was composed of many irregular nanosheets that were assembled together by weak interactions. The as-prepared materials were characterized by X-ray diffraction, thermogravimetric analysis, differential scanning calorimetry, scanning electron microscopy, transmission electron microscopy with selected area electron diffraction patterns, N-2 sorption, temperature-programmed reduction with CO, X-ray photoelectron spectroscopy (XPS), and in situ Fourier transform infrared (FT-IR) for CO adsorption. The catalytic behaviors for CO oxidation were studied by using a fixed bed microreactor. Compared to NiO nanoparticles, we found the flower-like NiO possessed a larger surface area, bimodal pore size distribution, higher reducibility, and superior catalytic activity for CO oxidation. The XPS and CO in situ FT-IR results showed that its catalytic property was morphology dependent. The flower-like morphology provided more coordinate unsaturated Ni atoms, more oxygen vacancies, and more defect sites, which made the flower-like NiO have a strong interaction with CO and more active sites for catalytic reactions. Further studies showed that a mild condition for thermodecomposition of the precursor was necessary to preserve the flower-like morphology because of the large discrepancy of the crystalline cell structures between the beta-Ni(OH)(2) precursor and product of NiO. |
| 關聯: | JOURNAL OF PHYSICAL CHEMISTRY C |
| 顯示於類別: | [化學工程與材料工程研究所] 期刊論文
|
文件中的檔案:
| 檔案 |
描述 |
大小 | 格式 | 瀏覽次數 |
|---|
| index.html | | 0Kb | HTML | 581 | 檢視/開啟 |
|
在NCUIR中所有的資料項目都受到原著作權保護.
|