MULTIPLE COATING OF TITANIUM-BORON OXIDE SOL-GEL ON GLASS

NCUIR > Engineering College > National Central University Department of Chemical & Materials Engineering > journal & Dissertation > Item 987654321/26732

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/26732

Title:	MULTIPLE COATING OF TITANIUM-BORON OXIDE SOL-GEL ON GLASS
Authors:	HSIEH,CW;CHIANG,AST;LEE,CC;TU,SL
Contributors:	化學工程與材料工程學系
Keywords:	N/A
Date:	1992
Issue Date:	2010-06-29 17:35:26 (UTC+8)
Publisher:	中央大學
Abstract:	TiO2 - B2O3 composite thin films have been coated on microscope slides by a multiple dip-coating technique. Films produced with heating steps between the deposition of successive layers exhibit a better optical quality than those without. The former have a smaller grain size, less than 30nm as measured by SEM, and therefore result in less transmittance loss at the short wavelength region. X-ray diffraction studies show that these films are amorphous even after 500-degrees-C calcination, while films produced without intermediate heating become slightly crystallized after the same treatment. The thickness of the coated film is proportional to the number of layers applied. A film about 200nm in thickness can be produced by just four coatings. The refractive index of the film is 2.23 as evaluated from the transmission spectrum.
Relation:	MATERIALS RESEARCH BULLETIN