    題名: Effect of heat treatment on the microstructure and mechanical properties of the consolidated Mg alloy AZ91D machined chips
    作者: Wu,HY;Hsu,CC;Won,JB;Sun,PH;Wang,JY;Lee,S;Chiu,CH;Torng,S
    貢獻者: 機械工程研究所
    關鍵詞: AL-ALLOYS;MAGNESIUM;MORPHOLOGY;EXTRUSION
    日期: 2009
    上傳時間: 2010-06-29 18:01:43 (UTC+8)
    出版者: 中央大學
    摘要: Influence of heat treatment on the properties of the consolidated AZ91D Mg alloy chips was performed in this study. The chips were pressed into a die to form a compact with a green density of 1.6g/cm(3). The 50-mm diameter green compact was then extruded into a 20-mm rod at 350 degrees C. The extruded rod was solution treated at a temperature of 415 degrees C for 24 h; the solution treated specimens were then aged at two temperatures: 170 and 215 degrees C. Heat treatments were conducted to explore the microstructure evolution and mechanical properties of the extruded rod. Heat treatments revealed that the age hardening effect was related to the transformation of the microstructure. Over aging during age heat treatment was believed to be caused by the formation of a lamellar structure composed of alternating layers Of Mg17Al12 phase and magnesium matrix. (c) 2008 Elsevier B.V. All rights reserved.
    關聯: JOURNAL OF MATERIALS PROCESSING TECHNOLOGY
    顯示於類別:[機械工程研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML480檢視/開啟


    在NCUIR中所有的資料項目都受到原著作權保護.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©  2006-2024  - 隱私權政策聲明