Impact fatigue of a polycarbonate/acrylonitrile-butadiene-styrene blend

NCU Institutional Repository > 工學院 > 機械工程研究所 > 期刊論文 > Item 987654321/26923

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26923

题名:	Impact fatigue of a polycarbonate/acrylonitrile-butadiene-styrene blend
作者:	Ho,MH;Hwang,JR;Doong,JL;Fung,CP
贡献者:	機械工程研究所
关键词:	MECHANICAL-PROPERTIES;RESIDUAL-STRESSES;COMPOSITES;POLYPROPYLENE;MORPHOLOGY;BEHAVIOR;POLYMERS;NYLON-6
日期:	1999
上传时间:	2010-06-29 18:03:22 (UTC+8)
出版者:	中央大學
摘要:	This study analyzes the impact properties of a polycarbonate/acrylonitrile-butadiene-styrene (PC/ABS) blend. The specimens were prepared under various injection molding conditions, including filling time, melting temperature, and mold temperature. Impact tests were performed with a Dynatup drop weight impact tester at different impact energies (10, 15, 20, 25 J). The fracture mechanism was examined with a scanning electron microscopy. The results indicated that the load-time history of the PC/ABS blend has approximately a sinusoidal form in impact. The best injection molding conditions are a filling time of 12 s, a melting temperature of 260 degrees C and a mold temperature of 80 degrees C. Tn this case, the specimen shows the highest energy absorbed in single impact, together with the highest impact number in impact fatigue. The impact number and the accumulation energy seem to follow an exponential curve as the impact energy decreases. The PC/ABS blend material clearly exhibited ductile fracture with a continuous reduction in strength by viscoplastic deformation. The higher the impact number, the higher the accumulation energy. The accumulation energy of impact fatigue with impact energy 10 J is about 35-45 times greater than the energy absorbed in single impact. Tearing, shear fracture, and plastic deformation are the major fracture mechanisms of the PC/ABS blend matrix in single impact and repeated impact conditions.