Wear and corrosion behaviors of SiCp reinforced copper matrix composite formed by hot pressing

NCUIR > Engineering College > Graduate Institute of Mechanical Engineering > journal & Dissertation > Item 987654321/26949

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/26949

Title:	Wear and corrosion behaviors of SiCp reinforced copper matrix composite formed by hot pressing
Authors:	Lee,YF;Lee,SL;Lin,JC
Contributors:	機械工程研究所
Keywords:	SLIDING WEAR;ALUMINUM
Date:	1999
Issue Date:	2010-06-29 18:03:57 (UTC+8)
Publisher:	中央大學
Abstract:	Wear and corrosion behaviors of SiCp reinforced copper matrix composite formed by hot pressing were studied. The results show that the tensile strength, hardness and material porosity increased with the increase of SiCp content. The wear rate of Cu/SiCp composites decreased with the increase of SiCp content, applied load and high sliding velocity (exceeds 300 rpm). In contrast the wear rate of Cu/SiCp composites increased with low sliding velocity (100 rpm to 300 rpm). A dramatic wear rate of Cu/SiCp, composite is observed at the initial wear stage (0-400m). However, when sliding distance exceeds 800 m, the wear behavior becomes more stable. In addition, the corrosion resistance of Cu/SiC, composite in 5% NaCl solution increases with increasing pH value, but decreases with increasing SiCp content. Pits always initiate at the interfacial boundary between SiCp and copper, which makes SiCp particles peeling and copper matrix pitting deeply.
Relation:	SCANDINAVIAN JOURNAL OF METALLURGY
Appears in Collections:	[Graduate Institute of Mechanical Engineering] journal & Dissertation

Files in This Item:

File	Description	Size	Format
index.html		0Kb	HTML	445	View/Open

社群 sharing