High-cycle fatigue of austempered ductile irons in various-sized Y-block castings

NCU Institutional Repository > 工學院 > 機械工程研究所 > 期刊論文 > Item 987654321/26996

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26996

题名:	High-cycle fatigue of austempered ductile irons in various-sized Y-block castings
作者:	Lin,CK;Wei,JY
贡献者:	機械工程學系
关键词:	MICROSTRUCTURE
日期:	1997
上传时间:	2010-06-29 18:05:08 (UTC+8)
出版者:	中央大學
摘要:	High-cycle fatigue (HCF) properties of a number of different grades of austempered ductile irons (ADIs) were investigated. Ductile irons were prepared as Y-block castings with three section sizes (25, 50, and 100 mm in thickness). Fatigue specimens were selected from various locations within the castings, austenitized at 1173 K, and then austempered at 573 and 633 K, respectively. HCF tests were conducted by rotary bending method to generate the S-N curves and the associated fatigue limits. As section size increased, the HCF strength of ADI was decreased and affected by the inferior graphite nodule morphology and microshrinkage porosity resulting from the slower solidification rate. The effects of section size, location within the heavy-section casting, and austempering temperatures on the HCF strength of ADI are interpreted in terms of the graphite nodule morphology and microshrinkage pores. An empirical equation was introduced to correlate the fatigue limit of ADI with the impact toughness value and mean nodule diameter.
關聯:	MATERIALS TRANSACTIONS JIM
显示于类别:	[機械工程研究所] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
index.html		0Kb	HTML	431	检视/开启

在NCUIR中所有的数据项都受到原著作权保护.

社群 sharing