The utilization of thin film transistor liquid crystal display waste glass as a pozzolanic material

NCU Institutional Repository > 工學院 > 環境工程研究所 > 期刊論文 > Item 987654321/27240

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/27240

题名:	The utilization of thin film transistor liquid crystal display waste glass as a pozzolanic material
作者:	Lin,KL;Huang,WJ;Shie,JL;Lee,TC;Wang,KS;Lee,CH
贡献者:	環境工程研究所
关键词:	MECHANICAL-PROPERTIES;CONCRETE
日期:	2009
上传时间:	2010-06-29 18:21:00 (UTC+8)
出版者:	中央大學
摘要:	This investigation elucidates the pozzolanic behavior of waste glass blended cement (WGBC) paste used in thin film transistor liquid crystal displays (TFT-LCD). X-ray diffraction (XRD) results demonstrate that the TFT-LCD waste glass was entirely non-crystalline. The leaching concentrations of the clay and TFT-LCD waste glass all met the current regulatory thresholds of the Taiwan EPA. The pozzolanic strength activity indices of TFT-LCD waste glass at 28 days and 56 days were 89% and 92%, respectively. Accordingly, this material can be regarded as a good pozzolanic material. The amount of TFT-LCD waste glass that is mixed into WGBC pastes affects the strength of the pastes. The strength of the paste clearly declined as the amount of TFT-LCD waste glass increased. XRD patterns indicated that the major difference was the presence of hydrates of calcium silicate (CSH, 2 theta = 32.1 degrees), aluminate and aluminosilicate, which was present in WGBC pastes. Portland cement may have increased the alkalinity of the solution and induced the decomposition of the glass phase network. WGBC pastes that contained 40% TFT-LCD waste glass have markedly lower gel/space ratios and exhibit less degree of hydration than ordinary Portland cement (OPC) pastes. The most satisfactory characteristics of the strength were observed when the mixing ratio of the TFT-LCD waste glass was 10%. (C) 2008 Elsevier B.V. All rights reserved.
關聯:	JOURNAL OF HAZARDOUS MATERIALS
显示于类别:	[環境工程研究所 ] 期刊論文