Temperature-Dependent Oxidation of Pt Nanoclusters on a Thin Film of Al2O3 on NiAl(100)

NCU Institutional Repository > 理學院 > 物理研究所 > 期刊論文 > Item 987654321/38984

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/38984

題名:	Temperature-Dependent Oxidation of Pt Nanoclusters on a Thin Film of Al2O3 on NiAl(100)
作者:	Luo,MF;Ten,MH;Wang,CC;Lin,WR;Ho,CY;Chang,BW;Wang,CT;Lin,YC;Hsu,YJ
貢獻者:	物理研究所
關鍵詞:	SCANNING-TUNNELING-MICROSCOPY;OXIDE-FILMS;AU-PT;GROWTH;AL2O3/NIAL(100);CLUSTERS;ALUMINA;METHANOL;SURFACE;GOLD
日期:	2009
上傳時間:	2010-07-08 14:01:17 (UTC+8)
出版者:	中央大學
摘要:	The temperature-dependent oxidation of Pt nanoclusters on a thin film of Al2O3 on NiAl(100), in the absence of a gaseous oxidizing agent, was investigated with various surface probe techniques, The Pt clusters (of mean diameter 2.2 tint and height 0.4 nm) grown from vapor deposition on the thin film of Al2O3 on NiAl(100) at 300 K became partially oxidized, as charge transfer from the Pt clusters to the oxide was indicated by a significant negative shift (0.4-0.5 eV) of binding energy (BE) of Al-ox 2p and O Is states from Al2O3. The oxidation of the cluster proceeded to a further level when the sample was annealed above 450 K; the Pt 4f(7/2) core level moved positively from BE 72.0 eV with increasing annealing temperature and eventually attained 72.6 eV above 650 K, which indicates a state of Pt2+. Accompanying this further oxidation, signals of both Al-ox 2p and O 1s shifted back to greater BE. The valence spectra indicate that the Pt-Al2O3 interaction was sustained whereas a new Pt-O bond was formed. Formation of a PtxAlyOz complex is proposed to explain the observations. The new Pt oxide binding was substantially stronger than the initial one, as was evident front the oxidized Clusters being resistant to sintering induced in electrochemical processes. The oxidation was associated also with a migration of oxide materials onto the Pt clusters, as both Al2O3(100) and NiAl(001) facets roughened after the annealing, and a probe of methanol adsorption showed no bare Pt clusters exposed but alumina-like structures on the surface.
關聯:	JOURNAL OF PHYSICAL CHEMISTRY C
顯示於類別:	[物理研究所] 期刊論文