Electrical and optical changes in the near surface of reactively ion etched n-GaN

NCU Institutional Repository > 理學院 > 物理研究所 > 期刊論文 > Item 987654321/39003

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/39003

题名:	Electrical and optical changes in the near surface of reactively ion etched n-GaN
作者:	Chen,JY;Pan,CJ;Chi,GC
贡献者:	物理研究所
关键词:	PHOTOLUMINESCENCE;HYDROGEN;MIXTURE;DAMAGE;INP
日期:	1999
上传时间:	2010-07-08 14:01:53 (UTC+8)
出版者:	中央大學
摘要:	Photoluminescence (PL) and ohmic contact resistance measurements were used to characterize the n-GaN surface treated with reactive ion etching (RIE). The n-GaN him was grown on a sapphire substrate by a metal organic chemical vapor deposition process. Subsequently, the GaN film was etched with BCl3 or Ar gas prior to the PL measurement and contact metal Ti/Al deposition. In PL spectra, we observed the peak shift of the impurity-related emission (yellow luminescence (YL)) for both BCl3 and Ar etched n-GaN films. The amount of this wavelength shift increases with the RIE rf power increase and depends on the species of the etching gases. The shift of the YL peak decreased after thermal annealing at 500 degrees C for 30 s. The YL peak shift may be attributed to the RIE induced surface point defects. In the ohmic contact resistance measurements, the transmission line model technique was used. The contact resistance of the RIE etched surface is around 5.4 x 10(-4) Omega cm(2). However, a lower contact resistance of 5.7 x 10(-6) Omega cm(2) was obtained for a native surface of n-GaN film. No obvious distinction between the roughness of etched and native GaN surfaces was observed by the atomic force microscope measurements. In an Xray grazing diffraction measurement, the crystalline lattice orientation and the coherent length of native n-GaN layer were better than the etched n-GaN according to the results of the rocking curve and Theta-2 Theta scan. (C) 1999 Elsevier Science Ltd. All rights reserved.
關聯:	SOLID-STATE ELECTRONICS
显示于类别:	[物理研究所] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
index.html		0Kb	HTML	409	检视/开启

在NCUIR中所有的数据项都受到原著作权保护.

社群 sharing

数据加载中.....