Screening, Manufacturing, Photoluminescence, and Molecular Recognition of Co-Crystals: Cytosine with Dicarboxylic Acids

NCU Institutional Repository > 工學院 > 化學工程與材料工程學系 > 期刊論文 > Item 987654321/49899

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/49899

题名:	Screening, Manufacturing, Photoluminescence, and Molecular Recognition of Co-Crystals: Cytosine with Dicarboxylic Acids
作者:	Lee,T;Wang,PY
贡献者:	化學工程與材料工程學系
日期:	2010
上传时间:	2012-03-27 16:25:55 (UTC+8)
出版者:	國立中央大學
摘要:	A workflow for screening and manufacturing co-crystals was used to produce 4:1 co-crystal of cytosine-oxalic acid dihydrate, 2:1 co-crystal of cytosine-malonic acid, and 2:1 co-crystal of cytosine-succinic acid with melting points of 270.2, 219.2, and 249.5 degrees C, and K(sp) values of 8.21 x 10(-12) m(5), 4.90 x 10(-5) m(3), and 3.11 x 10(-6) m(3) in water at 25 degrees C, respectively. 4:1 co-crystal of cytosine-oxalic acid dihydrate crystallized in the P2(1)/c space group. Both 2:1 co-crystal of cytosine-malonic acid and 2:1 co-crystal of cytosine-succinic acid crystallized in the P (1) over bar space group. Co-crystals of cytosine with dicarboxylic acids all possessed it self-assembled cyclic pattern of R(2)(2)(12) forming by a pair of N-H center dot center dot center dot O hydrogen bonds within a dimeric motif of cytosine. The self-recognition pairing of cytosine here resembled the standard hydrogen bonding pattern in the Watson-Crick complementary base pairing of guanine and cytosine but without the middle N-H center dot center dot center dot N interaction. Both photoluminescence (PL) emission intensity and the solubility of co-crystals at a given temperature followed the same descending order of 2:1 co-crystal of cytosine-malonic acid > 2:1 co-crystal of cytosine-succinic acid > 4:1 co-crystal of cytosine-oxalic acid dihydrate. The weakening of the hydrogen bonding strength of 2:1 co-crystal of cytosine-malonic acid due to the angling of the interlayers might explain its lowest melting point of 219.2 degrees C, its highest solubility and its highest PL emission intensity.
關聯:	CRYSTAL GROWTH & DESIGN
显示于类别:	[化學工程與材料工程學系 ] 期刊論文