Preparation of humidity-controlling porous ceramics from volcanic ash and waste glass

NCU Institutional Repository > 工學院 > 環境工程研究所 > 期刊論文 > Item 987654321/50165

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/50165

題名:	Preparation of humidity-controlling porous ceramics from volcanic ash and waste glass
作者:	Vu,DH;Wang,KS;Nam,BX;Bac,BH;Chu,TC
貢獻者:	環境工程研究所
關鍵詞:	WATER-VAPOR ADSORPTION;ACTIVATED CARBON;MICROSTRUCTURE DEVELOPMENT;MOISTURE ABSORPTION;PORE DISTRIBUTION;BEHAVIOR;ALLOPHANE;POWDERS;PARTICLES;SEPIOLITE
日期:	2011
上傳時間:	2012-03-27 17:05:07 (UTC+8)
出版者:	國立中央大學
摘要:	This work investigated the preparation of a humidity-controlling porous ceramic via sintering of a mixture of volcanic ash soil and waste glass at 800-815 degrees C for 5-10 min. The final products were analyzed to identify the porous and mechanical properties, the moisture adsorption-desorption performance characteristics, and the adsorbed moisture amount. The most superior ceramic product, manufactured by mixing 30% weathered volcanic ash and 70% waste glass, was sintered at 800 degrees C for 5 min. The porous properties included a BET surface area of 163.73 +/- 12 m(2)/g, porosity of 52.08 +/- 2.1%, and a pore size of approximately 9 nm in diameter. The total amount of water adsorbed by the superior ceramic product was 0.047 cm(3)/g. In addition, the mechanical characteristics, including a bulk density of 1.34 +/- 0.2 g/cm(3), 2.61 +/- 0.1% shrinkage, 4.64 +/- 0.3% ignition loss, and 6.58 +/- 0.4 MPa bending strength, are consistent with those of commercial porous ceramics. The leaching concentration of heavy metals in the final products were all well below the TCLP regulation limits. Thus, the most superior products meet the standards for commercial porous ceramics. (C) 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.