Constituted oxides/nitrides on nitriding 304, 430 and 17-4 PH stainless steel in salt baths over the temperature range 723 to 923 K

NCUIR > Engineering College > Departmant of Mechanical Engineering > journal & Dissertation > Item 987654321/50205

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/50205

Title:	Constituted oxides/nitrides on nitriding 304, 430 and 17-4 PH stainless steel in salt baths over the temperature range 723 to 923 K
Authors:	Shih,TS;Huang,YS;Chen,CF
Contributors:	機械工程學系
Keywords:	POST-OXIDATION PROCESS;SURFACE MICROSTRUCTURE;XPS;NITROGEN;QPQ;CARBON;FILMS;ESCA;AES
Date:	2011
Issue Date:	2012-03-27 17:06:25 (UTC+8)
Publisher:	國立中央大學
Abstract:	The progressively developed oxides and nitrides that form on nitriding 304, 430 and 17-4 PH stainless steel are analysed by X-ray Diffraction (XRD) and X-ray Photoelectron Spectroscopy (XPS) in this study. The experimental results show that the Cr contents and matrix structures (ferrite, austenite and martensite) play an important role in forming FeCr(2)O(4), Cr(2)O(3) and Fe(2)O(3) oxides as well as nitrides. After a short immersion time, oxides of Cr(2)O(3) and FeCr(2)O(4) form in nitride films on 304 stainless steel samples. Fe(2)O(3) oxide will subsequently form following an increasing immersion time. For the 430 stainless steel, Cr(2)O(3) predominately forms after a short dipping time which hinders the growth of the nitride layer. As a result, this sample had the thinnest nitride film of the three for a given immersion time. After the formation of oxides, both CrN and Cr(2)N were detected near the surface of the nitride films of three samples while Cr(2)N phases formed in the deeper zone. The greatest amount of Fe(2)O(3) oxide among the three samples was obtained on the nitriding 17-4 PH stainless steel which also had a high intensity count of N 1s. (C) 2011 Elsevier B. V. All rights reserved.
Relation:	APPLIED SURFACE SCIENCE
Appears in Collections:	[Departmant of Mechanical Engineering ] journal & Dissertation

Files in This Item:

File	Description	Size	Format
index.html		0Kb	HTML	502	View/Open

社群 sharing

Loading...