Influence of annealing temperature on the structural, optical and mechanical properties of ALD-derived ZnO thin films

NCU Institutional Repository > 工學院 > 機械工程學系 > 期刊論文 > Item 987654321/50243

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/50243

题名:	Influence of annealing temperature on the structural, optical and mechanical properties of ALD-derived ZnO thin films
作者:	Yen,CY;Jian,SR;Chen,GJ;Lin,CM;Lee,HY;Ke,WC;Liao,YY;Yang,PF;Wang,CT;Lai,YS;Jang,JSC;Juang,JY
贡献者:	機械工程學系
关键词:	CATALYST-FREE SYNTHESIS;NANOINDENTATION;NANOWIRES;SAPPHIRE;EPITAXY
日期:	2011
上传时间:	2012-03-27 17:07:28 (UTC+8)
出版者:	國立中央大學
摘要:	ZnO thin films grown on Si(1 1 1) substrates by using atomic layer deposition (ALD) were annealed at the temperatures ranging from 300 to 500 degrees C. The X-ray diffraction (XRD) results show that the annealed ZnO thin films are highly (0 0 2)-oriented, indicating a well ordered microstructure. The film surface examined by the atomic force microscopy (AFM), however, indicated that the roughness increases with increasing annealing temperature. The photoluminescence (PL) spectrum showed that the intensity of UV emission was strongest for films annealed at 500 degrees C. The mechanical properties of the resultant ZnO thin films investigated by nanoindentation reveal that the hardness decreases from 9.2 GPa to 7.2 GPa for films annealed at 300 degrees C and 500 degrees C, respectively. On the other hand, the Young's modulus for the former is 168.6 GPa as compared to a value of 139.5 GPa for the latter. Moreover, the relationship between the hardness and film grain size appear to follow closely with the Hall-Petch equation. (C) 2011 Elsevier B. V. All rights reserved.
關聯:	APPLIED SURFACE SCIENCE