Reflection High-Energy Electron Diffraction Characterization of Cobalt Clusters Electrodeposited on a Au(100) Electrode

NCU Institutional Repository > 理學院 > 化學學系 > 期刊論文 > Item 987654321/50785

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/50785

题名:	Reflection High-Energy Electron Diffraction Characterization of Cobalt Clusters Electrodeposited on a Au(100) Electrode
作者:	Wu,HL;Zei,MC;Yau,SL
贡献者:	化學學系
关键词:	IN-SITU STM;EPITAXIAL-GROWTH;THIN-FILMS;GOLD ELECTRODE;CO CLUSTERS;PART I;NUCLEATION;AU(111);SURFACES;MICROSCOPY
日期:	2010
上传时间:	2012-03-27 18:10:07 (UTC+8)
出版者:	國立中央大學
摘要:	Cobalt was electrodeposited onto a reconstructed Au(100) electrode in 0.25 M Na(2)SO(4) + 0.1 mM CoSO(4) under potentiostatic conditions. The Au(100) electrode loaded with the Co deposit was transferred via an argon environment to ultrahigh vacuum and subsequently examined with reflection high-energy electron diffraction (RHEED). The resultant RHEED results were analyzed in detail to unveil the structures of the as-prepared Co deposit, which assumed nanometer-sized clusters on the Au(100) substrate. Aided by coulometric results, profile analysis of the RHEED results indicated that the Co clusters on average were 3 nm in width and 15 atomic layers in height. The packing habits of the Co clusters, determined by the obtained RHEED results, were the face-centered cubic (fcc) phase, rather than the hexagonal closed-packed (hcp) phase. Cobalt clusters grew with their fcc ((1) over bar 10) plane aligned parallel to the Au(100) substrate and with their [110] axis aligned in the [011] direction of the Au(100) substrate. The preferential growth of the fcc Co phase is driven by the optimal lattice match between the ((1) over bar 10) plane of Co clusters and the Au(100) substrate network.