    題名: 不鏽鋼與鋁合金之擴散接合研究;Parameters Study of Stainless Steel and Aluminum Alloy Diffusion Bonding Aiming
    作者: 吳哲穎;Wu, Che-Ying
    貢獻者: 機械工程學系在職專班
    關鍵詞: 擴散接合;拉伸試驗;不鏽鋼316L;不鏽鋼430;鋁合金6061-T6;Diffusion Bonding;Tensile Testing;Stainless Steel 316L;Stainless Steel 430;Aluminum Alloy 6061-T6
    日期: 2022-08-29
    上傳時間: 2022-10-04 12:11:53 (UTC+8)
    出版者: 國立中央大學
    摘要: 本研究延續先前不鏽鋼擴散接合實驗,並新增不鏽鋼430與鋁合金6061來進行擴散接合之實驗,研究不同材質之擴散焊接合參數,例如:溫度(Temperature)、施加壓力(Pressure)及時間(Time)。當擴散接合完成後,先探討不同的擴散接合參數所造成的壓縮量大小,嘗試找出影響擴散接合後壓縮率的關鍵參數。再來進行拉伸試驗確認接合面的接合強度,更新增了接合面與拉力方向平行之試片與剪力試片來探討鈑片之間的徑向受力程度。進行拉伸試片後求得各種擴散接合試塊的最大拉伸應力值(Max Stress),與伸長率(Percentage of Elongation),並將母材料進行相同的拉伸實驗後與擴散接合試片進行機械性質的比較,得以各擴散接合試片的接合強度,用以判斷擴散接合的最佳結合參數。;This study continues the previous stainless steel diffusion bonding experiment, adding stainless steel 430 and aluminum alloy 6061 to perform the diffusion bonding experiment to study the diffusion bonding parameters of various materials such as temperature, pressure and time. After the diffusion bonding is complete, we will first discuss the amount of compression caused by the various diffusion bonding parameters and try to find important parameters that affect the compressibility after diffusion bonding. Next, a tensile test was carried out to confirm the joint strength of the joint surface, and a shear force test piece in which the test piece and the joint surface were parallel to the tensile force direction was added, and the radial force between the sheets was examined. After stretching the test pieces, the maximum tensile stress (maximum stress) and elongation (elongation rate) of various diffusion bond test pieces were obtained. Optimal bonding ratio for diffusion bonding using the bonding strength of the diffusion bonding test piece by comparing the properties.
    顯示於類別:[機械工程學系碩士在職專班 ] 博碩士論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML99檢視/開啟


    在NCUIR中所有的資料項目都受到原著作權保護.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 隱私權政策聲明