利用改質石墨烯修飾電極以提高電池在高電壓 下的性能和穩定性;Modification of the current collector with graphene to enhance the performance and stability of batteries at high voltage

NCUIR > Engineering College > Energy of Mechatronics > Electronic Thesis & Dissertation > Item 987654321/92664

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/92664

Title:	利用改質石墨烯修飾電極以提高電池在高電壓下的性能和穩定性;Modification of the current collector with graphene to enhance the performance and stability of batteries at high voltage
Authors:	格維克;GLANIC, Victor Nicolas LE
Contributors:	能源工程研究所
Keywords:	儲能;鋰離子電池;石墨烯;防腐;奈米材料;energy storage;Li-ion batteries;graphene;anti-corrosion;nanomaterial
Date:	2023-09-21
Issue Date:	2024-09-19 16:11:38 (UTC+8)
Publisher:	國立中央大學
Abstract:	鋰離子電池如今在能量存儲方面得到了廣泛的投資，無論是用於嵌入式設備還是固定應用。這些電池在零售市場上擁有最佳的電氣性能。從製造出來的那一刻起，日曆和循環老化都會影響鋰離子電池的性能。老化過程的一個重要部分是電流收集器的腐蝕，特別是在正極的鋁基底的情況下尤為明顯。一般來說，鋁由於形成了不透水的原生氧化鋁膜而能夠抵抗腐蝕。然而，在某些電化學條件下，腐蝕會影響電流收集器的界面。這在高壓鋰離子電池的情況下尤為明顯，這些電池更容易受到腐蝕的影響。許多防腐策略已被提出。以往關於通過電化學剝離法製備的氟化石墨烯（FG）的研究表明，這種氟化電化學剝離石墨烯（F-ECG）似乎是一種有希望的疏水材料，可以解決腐蝕問題，同時通過石墨烯的獨特性能提高鋁電池電流收集器的電氣性能。本研究展示了應用基於石墨烯的材料於能量存儲設備的調查，重點關注負極鋁電池電流收集器。其結果展示了石墨烯基材料應用於儲能裝置的研究，重點關注負極鋁電池集流體。通過 EPD 在織構鋁箔上逐層塗覆不同結構的保護膜，然後分析其形貌、厚度、元素組成以及 LSV 電化學和半電池表徵。結果表明，雙層 F-ECG 500s 和 F-ECG 700s EPD 持續時間的特定條件允許達到 1.63V 的電位極限，這表明與其他無塗層鋁蝕刻樣品相比，腐蝕保護得到了改善。單層 F-ECG 的半電池測試表明，該結果表明，所提出的 Al 上的 FECG 改性劑有助於提高循環穩定性，這為未來高性能 LIB 鋪平了道路.;Lithium-ion batteries are nowadays widely invested in term of energy storage whether for embedded devices or stationary applications. Those batteries have the best electrical properties available on the retail market. The unstable cycle stability affects the performance of the lithium-ion batteries from the moment they are manufactured. An important process that occurs as a part of the ageing is corrosion of the current collectors, especially prominent in the case of the aluminum substrate for the positive electrode. Generally, aluminum resists corrosion due to the formation of a non-permeable film of native aluminum oxide. Nevertheless, at certain electrochemical conditions corrosion affects the interface of the current collector. This is especially the case for high-voltage lithium-ion batteries which are more affected by the corrosion affect. Many strategies of anti-corrosion have been proposed. Previous works on fluorinated graphene (FG) obtained by fluorination of the electrochemically exfoliated graphene (F-ECG) seems to be a promising hydrophobic material to solve corrosion issue while increasing the electrical properties of aluminum batteries current collector thank to graphene unique properties. This work shows the investigation of graphene-based material applied to energy storage devices focusing on the negative aluminum battery current collector. The different iii structures of protective film were layer-by-layer coated on the textured Al foil by EPD, then we analysis the morphology, thickness, elemental composition and the LSV electrochemical as well as the half-cell characterization. Result show that the specific condition of dual layer F-ECG 500s and F-ECG 700s EPD duration allows to achieve a potential limit of 1.63V, suggesting the improved corrosion protection compared to other non-coated aluminum etched sample. The half-cell testing with single layer F-ECG shows that this result shows that the proposed FECG modifier on the Al can help to increase the cycling stability, which pay a way toward performant LIB in the future.